RESUMO
Flexible conductive-bridging random-access-memory (RAM) cells were fabricated with a cross-bar memory cell stacked with a top Ag electrode, conductive polymer (poly(n-vinylcarbazole): PVK), electrolyte (polyethylene oxide: PEO), bottom Pt electrode, and flexible substrate (polyethersulfone: PES), exhibiting the bipolar switching behavior of resistive random access memory (ReRAM). The cell also exhibited bending-fatigue-free nonvolatile memory characteristics: i.e., a set voltage of 1.0 V, a reset voltage of -1.6 V, retention time of >1 × 10(5) s with a memory margin of 9.2 × 10(5), program/erase endurance cycles of >10(2) with a memory margin of 8.4 × 10(5), and bending-fatigue-free cycles of â¼1 × 10(3) with a memory margin (I(on)/I(off)) of 3.3 × 10(5).
RESUMO
Silicon solar cells mainly absorb visible light, although the sun emits ultraviolet (UV), visible, and infrared light. Because the surface reflectance of a textured surface with SiNX film on a silicon solar cell in the UV wavelength region (250-450 nm) is higher than â¼27%, silicon solar-cells cannot effectively convert UV light into photo-voltaic power. We implemented the concept of energy-down-shift using CdSe/ZnS core/shell quantum-dots (QDs) on p-type silicon solar-cells to absorb more UV light. CdSe/ZnS core/shell QDs demonstrated clear evidence of energy-down-shift, which absorbed UV light and emitted green-light photoluminescence signals at a wavelength of 542 nm. The implementation of 0.2 wt% (8.8 nm QDs layer) green-light emitting CdSe/ZnS core/shell QDs reduced the surface reflectance of the textured surface with SiNX film on a silicon solar-cell from 27% to 15% and enhanced the external quantum efficiency (EQE) of silicon solar-cells to around 30% in the UV wavelength region, thereby enhancing the power conversion efficiency (PCE) for p-type silicon solar-cells by 5.5%.